Metallic Materials Vol. 55 (2017), no. 4, pp.255-265

Title: Effect of deposition potential and copper concentration on the phase transformation mechanism and structural distribution during electrodeposition of Ni-Cu magnetic alloy thin films
Author: P. NATH, R. PANDEY, A. DAS, A. MALLIK
Abstract: Ni-Cu alloy thin films were electroplated onto graphite substrates in three electrode setup at varying applied overpotentials of –1.4, –1.5, and –1.6 V with an approximate Cu:Ni ratio of 1:20, 1:15, and 1:11 where the concentration of Ni was 0.175 M, and Cu were 0.009 M, 0.012 M, 0.015 M, respectively. The cyclic voltammetry experiments reveal that during the co-reduction of Cu and Ni there was no distinct peak. However, the dissolution had taken place with absolute anodic peaks for corresponding elements. Morphological results showed there was a transition from wavy layered structure to the nodular structure with an increase in deposition potential and Cu concentration in the bath. The compositional analysis revealed that the film was getting richer in Ni with an increase in deposition potential and a decrease in Cu ion concentration in the electrolyte bath. Magnetic Force Microscopy (MFM) technique indicated that there was a definite and distinct impact of deposition potential and composition on the distribution of magnetic phase in the alloy film.
Keywords: Ni-Cu alloy, thin film, Magnetic Force Microscopy (MFM), electrodeposition, cyclic voltammetry
Published online: 22-Aug-2017
Year: 2017, Volume: 55, Issue: 4 Page From: 255, Page To: 265
doi:10.4149/km_2017_4_255