Bratislava Medical Journal Endocrine Regulations General Physiology and Biophysics Neoplasma Acta Virologica Studia Psychologica Cardiology Letters Psychológia a patopsych. dieťaťa Kovove Materialy-Metallic Materials 2021 2020 2019 2018 2017 2016 2015 2014 2013 2012 2011 2010 Slovenská hudbaWebshop Cart
Your Cart is currently empty.
Info: Your browser does not accept cookies. To put products into your cart and purchase them you need to enable cookies.
Metallic Materials Vol. 51 (2013), no. 6, pp.367-371 |
||
Title: Compaction and solid state sintering behavior of Cu-20%wt ZnO powders | ||
Author: M. ARDESTANI | ||
Abstract: In this research, compaction behavior and solid state sinterability of Cu-20 wt.% ZnO powders were investigated. The compressibility of the powders was evaluated using Heckel and Panelli -Ambrosio equations. The powders were compacted uniaxially by 50,100, 200 and 300 MPa at room temperature. The cold compacted powders were sintered at 850 and 1000 °C. The results showed that by increasing cold compaction pressure and sintering temperature the density of sintered compacts improved significantly. Additionally, it was found that the largest increase of density during sintering process was observed in the samples with relatively low green densities. The microstructural evaluation of the sintered samples by Scanning Electron Microscopy (SEM) demonstrated that increasing the sintering temperature and cold compaction pressure resulted in decreasing the volume fraction of the pores and also their dimensions. However, it was confirmed that sintering temperature had more effective role on elimination of porosities rather than cold compaction pressure. The highest density was achieved for the samples which were compacted by 300 MPa and sintered at 1000 °C. |
||
Keywords: metal matrix composites (MMC), powder consolidation, sintering | ||
Published online: 20-Sep-2017 | ||
Year: 2013, Volume: 51, Issue: 6 | Page From: 367, Page To: 371 | |
doi:10.4149/km_2013_6_367 |
||