Bratislava Medical Journal Endocrine Regulations General Physiology and Biophysics Neoplasma Acta Virologica Studia Psychologica Cardiology Letters Psychológia a patopsych. dieťaťa Kovove Materialy-Metallic Materials 2021 2020 2019 2018 2017 2016 2015 2014 2013 2012 2011 2010 Slovenská hudbaWebshop Cart
Your Cart is currently empty.
Info: Your browser does not accept cookies. To put products into your cart and purchase them you need to enable cookies.
Metallic Materials Vol. 55 (2017), no. 3, pp.161-167 |
||
Title: Influence of cold forging and annealing on microstructure and mechanical properties of a high-Mn TWIP steel | ||
Author: P. KUSAKIN, A. KALINENKO, K. TSUZAKI, A. BELYAKOV, R. KAIBYSHEV | ||
Abstract: The influence of cold biaxial forging and annealing on the microstructure evolution and mechanical properties of Fe-18Mn-0.6C-0.1N TWIP steel was investigated. The microstructure after thermomechanical treatment was examined by means of scanning electron microscopy (SEM) with electron back-scattered diffraction (EBSD) analyzer and transmission electron microscopy (TEM). The microstructure containing a high density of deformation twins was evolved by cold forging. Then, the deformation microstructure was recovered or partially recrystallized during subsequent annealing for 1 h at 673 or 873 K, respectively. The cold biaxial forging followed by partial recrystallization resulted in a very attractive combination of mechanical properties. The yield strength and the ultimate tensile strength of the steel after cold biaxial forging were 1320 and 1540 MPa, respectively, with elongation of 6 %. On the other hand, the yield and ultimate tensile strength of 770 and 1110 MPa, respectively, and elongation about 40 % were obtained after partial recrystallization. The as-forged and recovery annealed samples showed fatigue limit of 600 and 550 MPa, respectively, and the sample after partial recrystallization showed slightly lower fatigue limit of 500 MPa. |
||
Keywords: TWIP-steel, deformation twinning, microstructure, mechanical properties, fatigue | ||
Published online: 06-Jun-2017 | ||
Year: 2017, Volume: 55, Issue: 3 | Page From: 161, Page To: 167 | |